High temperature wear-resistant breathable brick

Field of technology:

This product belongs to the technology field of refractory material, in particular to a high temperature wear-resistant breathable brick and its production method.

 

Background technology:

The current wear-resistant breathable brick has good gas permeability and good resistance performance of splat cooling and thermal shock. However, after the boiler quickly stops, the current wear-resistant breathable brick will broke. In addition, this kind of brick will break if cold wind is brought into the boiler when materials are fed into the lime kiln. Therefore, it is necessary to design a kind of breathable brick with good high temperature and wear resistance.

 

Content of this product:

The technical problem solved by this product is that it overcomes the shortcomings of the current technology and provides a high temperature wear resistant brick. This product effectively avoid the breaking of the wear-resistant breathable brick caused by the quick stopping of the kiln and the cold wind brought into the kiln when materials are fed into the lime kiln.

Another technical problem it resolves is that it provides the production method. The high temperature wear-resistant breathable brick made through this method only needs rapid drying other than firing.

 

The production method of the high temperature wear-resistant breathable brick is characterized in the following steps:

(1). Weigh and take the raw material of high aluminum, corundum, silicon carbide, metallic silicon, metal aluminum, explosion-proof fiber, phosphoric acid, clay, graphite powder and asphalt powder according to the above-mentioned ratio for standby;

(2). Dilute the phosphoric acid with water, wetly grind the mixture of the dilute phosphoric acid solution and the high alumina, corundum, silicon carbide and clay and keep it for 24 hours;

(3). Add metal silicon, metal aluminum, graphite powder, explosion-proof fiber and asphalt powder into the mixture made through step (2). Wetly grind it again and compress it into the shape with the brick machine. The high temperature wear-resistant breathable brick will be made after drying in the 200℃.

The high temperature wear-resistant breathable brick of this invention has good resistance performance of splat cooling and thermal shock and good corrosion resistance performance, which not only saves energy, but also greatly reduces the production time. The high temperature wear-resistant breathable brick made through this method only needs rapid drying other than firing.

 

Brief description of the drawings:

The following drawing is the production flow chart of the high temperature wear-resistant breathable brick.

Brief description of the drawings

Embodiment:

Hereinafter, the above-described contents of the present invention are described in further detail with reference to specific embodiments. It should not be understood that the scope of the above subject matter of the present invention is limited to the following examples. All techniques based on the above content of the present invention are within the scope of the present invention.